Technical specification for Thermostone block adhesive

Given that the raw material for Beast mortar plaster (zeolite) is a porous rock that is full of air gaps, which amounts to 50% of the volume, and the size of the voids ranges between 2-7 angstram, as the square meter contains 1200 meters of channels and air gaps in which air is trapped. In turn, it impedes the transfer of heat through it, as static air is one of the most heat-insulating materials, as the thermal conductivity, according to the Royal Scientific Society tests, reached 0.270 (W / m ᴼ h) (*), and according to British Standard No. BS EN 1745

The chemical properties of Beast mortar plaster, which are represented by - surface tension - surface porosity - adsorption, and low thermal conductivity, make thermoplastic plaster ideal in resisting moisture as it works unlike other insulators, as it attracts oxygen and hydrogen atoms due to the surface tension property over huge areas From its crystalline formation due to the porosity of the surface and it re-releases oxygen and hydrogen atoms when the medium needs them due to the adsorption property. As for other insulators, they close the surface pores, which leads to the formation of moisture on the outer surfaces.

The nature of the chemical properties of zeolite mineral and the inability to form internal or surface moisture makes the possibility of the formation of parasites, mold and germs not possible.

The adoption of Beast mortar plaster on pozzolana metal, which is characterized by open, multi-surface, rough hair cells, with a size of 50% of the total volume, which enables it to absorb most of the sound waves falling on it, as it has a very high sound absorption coefficient, according to the American standard ASTM C423

The physical composition of zeolite mineral (pozzalana) with high hardness (4) and its mechanical properties, which are represented by the bonding factor between the silica particles and the property of not shrinking and falling due to the structural structure of the aluminum and titanium units, hydrophobic, and its combination with silicon shows a high resistance to external mechanical influences such as shocks and vibrations and internal factors of landing and And contraction - expansion and contraction factor (000.1)%.

The reasons why Beast mortar plaster bears high temperatures is because it contains a large percentage of non-combustible scoria, in addition to the volcanic origin of the zeolite mineral, which makes its resistance to high temperatures ideal, as it is used in many uses for metal melting furnaces, stoves, boiler rooms, and fire-resistant buildings, as it has reached the strength of heat tolerance According to the tests of the University of Science and Technology, reference No. (38), it reached 400 degrees Celsius, and according to the American Standard No. ACTM E 119-

The blocks / panels / walls must be free of impurities such as dust or other small particles on the surfaces and the walls must be moistened with pure water, with a temperature of 5-35 degrees Celsius when used.

Apply Beast mortar on all concrete surfaces as a final coating layer with a thickness of 3-5 mm and the thickness can be increased as needed using conventional plastering tools or plastering machines. It can be applied directly to bricks or concrete and can be applied as a final face.

Beast mortar is supplied in plastic bags of 25 kg/35 kg. Store the product in a clean, dry area protected from direct sunlight and extreme heat and cold. Opened bags should be used first. Unopened bags can be stored for 12 months. Use the oldest material first.

A dry, thin-layer, cement-based plaster product with a fine grain gradient of 25 micron - 1.2 mm, plaster for blocks, cellular / lightweight concrete slabs and other concrete surfaces. Additives are plasticizing agents, adhesion-enhancing agent and water-retaining agents.

Beast mortar should always be applied in accordance with the method given in this technical data sheet. The Company is not liable for any claim arising from non-performance of the product due to improper procedure or use of the product for a purpose not recommended. Please contact the company's technical team for more details on the Beast mortar application

The product is not considered dangerous goods during transportation.

Shelf life is 12 months when stored in dry conditions at normal temperature and humidity.

Mixing thoroughly with the recommended amount of drinking water, using a high-speed or hand mixer, allow the substance to react for 5 minutes before application.

• A dry, thin-layer, cement-based plaster product with a fine grain grade of 25 microns - 1.2 mm.
• Plaster for cellular/lightweight concrete blocks and panels and other concrete surfaces.
• Additives are plasticizing agents, adhesion-enhancing agent and water-retaining agents.

density	1.50 kg/Itr
Initial tensile strength	1.8 Nmm² - 2007:JS921
thermal conductivity	W/M.K 0.26
compressive strength	14.3 N/mm² with an average of 28 days
granular gradient	25 microns - 1.2 mm
tensile strength	6.3 N/mm² with an average of 28 days
maximum application time	60 minutes at + 30 ° C
application temperature	+5°C to +40°C
Consumption	w 5 - 4 kg / m² for brickwork
Mixing water rate	6.5-6 25 kg/L
the color	grey/white
Storage	1 year
Packing	35/25 kg

Chemical Composition
Thermal Cement
SIO2
AL2O3
Fe2O3
MGO
Ca(OH)2
CAO
TIO2

• Excellent workability to allow for longer working periods
• Resistant to mold, parasites, germs, salts, sulfates and oxidation
• Economical costs Minimum amount of use, which reduces material costs
• Better self-treatment water retention properties

• High bond strength, 10 times the normal bleachers
• Shrinkage, stretching and slip resistance
• Quick setup time
• Increases the speed of construction, only 24 hours is required before the next stage such as plaster, paint, etc